    Nylon 6 Brittle parts

    Hi every one, I am not so experinced at Injection molding, we are facing an issue with a new part for us, the parts are brittle and the issue was just discovered. Several process changes has been done but the issue remains almost in the same level. Any advice you can provide?
    Thanks in advance

  2. #2
    Join Date
    Feb 2022
    Posts
    7

    Re: Nylon 6 Brittle parts

    Unfortunately Nylon is a hygroscopic material. It will dry out and become brittle. In the past I have worked at places where we had to add water to the parts just before shipping so this would not happen. It has been a long time since I worked with nylon so maybe someone can suggest an additive or possible an alloy to help you. I would talk to your material rep on this issue.

  3. #3
    Join Date
    Dec 2012
    Location
    Serbia
    Posts
    107

    Re: Nylon 6 Brittle parts

    We are using climatic chamber where we put parts after molding on 24h, 90% humidity and 55C. After process they are more flexible and harder to brake.
    So far we have good resaults with this metod.

  4. #4

    Re: Nylon 6 Brittle parts

    Equally important is to make sure you are not over drying the material prior to production. A nylon 6/6 or heat stabilized nylon may yield better performance.