Round pieces injection resulting squared problem
We have created an injection mould for round sticks. After injecting with several materials with different melt flow index, changing prsuure, temperatures, injection speed, etc all the pieces turn out to be squared, with the diagonal bigger then the diameter set in the mould erosion.
Do you have any advice in what could us be doing wrong, or what probably we did wrong.
Thanks in advance for any advice