11th March 2021, 11:09 AM
#1
Back Pressure
When we should use back pressure?
How does it affect the product?
-
13th March 2021, 03:32 PM
#2
Re: Back Pressure
You should always add Back Pressure. There is a way to set back pressure but for now since you are a beginner, set it to about 7000 Plastic Psi or about 700 hydraulic psi.
If you do not add back pressure you can have splay on the parts. You can also have shot to shot inconsistency.
Suhas
-
18th March 2021, 09:09 AM
#3
Re: Back Pressure
Depending on what molding machine your working with you will likely be limited to approximate 300 psi maximum (hydraulic pressure), 150 to 200 psi of back pressure is typically a good range for most materials. Back pressure is intended to provide some resistance against the screw during shot size recovery to improve the melt and shot size consistency as Suhas stated. Excessively high back pressures will introduce greater wear on the screw tip and check ring.
-
22nd March 2021, 10:49 AM
#4
Re: Back Pressure
Usually there is recommended values for back preassure in material datasheet. Is most of the time OK value.
-
7th June 2021, 05:27 AM
#5
Re: Back Pressure
As the above have stated back pressure should always be used. When using a natural material and a master batch/pigment back pressure will help these mix into a uniform colour.
-
9th November 2021, 12:26 PM
#6
Re: Back Pressure
I make closures, high cavitation molds (32, 64, 72, 96, cavities), hot runner systems. A lot of the processors don't use back pressure because it results in gate strings that are difficult to remedy. How can I fix this to show the others how it could be a benefit.
-
10th November 2021, 03:54 AM
#7
Re: Back Pressure
What benefit are you hoping to get by changing the process?
-
5th December 2021, 06:43 PM
#8
Re: Back Pressure
Do you have a shut off nozzle? Without it, and without the proper software in some machines, you cannot continue to recover the screw while the mold opens and the parts are ejected; for the absolute fastest cycle times. You leave the nozzle open, while you decompress the screw, shut the nozzle, and you can recover the screw while the mold opens, ejects parts, and even closes back.
To do this properly, you need more than one motor/pump on a hydraulic press (one runs clamp and the other the injection unit) or on a hybrid you need electric screw drive!
Back pressure is a MUST for a stable process AND consistent dimensions!
Rick
-
5th December 2021, 06:44 PM
#9
Re: Back Pressure
Do you have a shut off nozzle? Without it, and without the proper software in some machines, you cannot continue to recover the screw while the mold opens and the parts are ejected; for the absolute fastest cycle times. You leave the nozzle open, while you decompress the screw, shut the nozzle, and you can recover the screw while the mold opens, ejects parts, and even closes back.
To do this properly, you need more than one motor/pump on a hydraulic press (one runs clamp and the other the injection unit) or on a hybrid you need electric screw drive!
Back pressure is a MUST for a stable process AND consistent dimensions!
Rick