FR Rated Materials
Does anyone have a presentation or write-up on the general guidelines for molding FR rated materials. Like what temperature does non-halogenated FR additives start to degrade and what other process setting, mold and part designs are detrimental?
-
21st February 2021, 02:20 AM
#2
Re: FR Rated Materials
Low shear, low residence time, good venting.
For mold design you may need a corrosion resistant coating or steel.
-
22nd February 2021, 10:29 AM
#3
Re: FR Rated Materials
the base is to have a propper drying and proper process temeratures You have to still have in the brain, that the material contain FR aditives, which are sensitive for temperature. If FR aditive during burning is releasing the gass. The FR can by started by temperature. Also high injection speed (high shear) can bring a silvering issue. This is a base for building of process.
Posting Permissions
- You may not post new threads
- You may not post replies
- You may not post attachments
- You may not edit your posts
-
Forum Rules