Thanks suhas
Hello,
Just wondering if anyone out there might have some suggestions
for medical grade PVC suppliers. We will be injection molding low
durometer, 50-70 PVC for our medical components.
Yes we are running the 74A. Thanks for the info. We are looking at adding more cores to increase our
cooling time. The longer the parts have to cool on the cores the better.
Also, I am working with other experienced molding personnel, 25+ years experience, and
they have never seen anything like this material. Drying time was about 2 days in hopper dryer
at 150 F, and...
The shrink we measured is overall part length. We processed at 430 F stock temp and 390 F stock temp (at nozzle) and the
shrink between the two was unreal. The part processed at the cooler temp. ...
I was wondering if anyone has any experience processing this type of resin.
It is a TPU (thermoplastic polyurethane) from Lubrizol. We are having issues
of excessive cure times. Our best parts...
I was wondering if anyone has any experience with Terlux. I was asked what the best hot tip
design is to use with this material. It is hard to find any info for this. Thanks.
Thanks for the help Suhas. I will be sure to post our finding on here.:)
I have a question on overmolding a new part. The scenario is as
follows: We will be injection molding pvc, 50 durometer from alpha
gary, onto a radel or ultem insert. We make the radel/ultem...