I was wondering if anyone has any experience with Terlux. I was asked what the best hot tip
design is to use with this material. It is hard to find any info for this. Thanks.
Printable View
I was wondering if anyone has any experience with Terlux. I was asked what the best hot tip
design is to use with this material. It is hard to find any info for this. Thanks.
I've ran their clear abs years ago for a pay phone coin chute. It ran well and didn't seem to be too shear sensitive. Now for the bad news: that was a cold runner mold. So I've never shot any from a hot runner.
Rick
We used PLASTHING from Italy. Parts were for a large OEM that made writing instruments. The mold had a sprue bushing that required a "dipping" nozzle on the press that fit into the bushing.
I really liked the hot runner/manifold!
KOM
brent
Terlux, is a methyl methacrylate / ABS. We found it a bit tricky. I seem to remember it getting rubbery, if over heated in any way.
KOM
brent
DME J-series and don't get over 25% rg it will be not to your advantage aesthetically