View Full Version : issue with molding of part using LEXAN 940
suresh.c
19th December 2017, 05:56 PM
need some Advise on improving finIsh quality of parts, WE ARE MOLDING THE PARTS IN LEXAN 940.. some funny looking marks appearing after molding.. not sure how to solve it,.. i would be grate ful for any advise to help solve it
thanks & regards suresh.c
Suhas
20th December 2017, 12:04 AM
Suresh,
Looks like there are notes on the side. They are all valid. The plastic is not flowing easy and evenly.
Suhas
Joel JS
20th December 2017, 08:51 PM
need some Advise on improving finIsh quality of parts, WE ARE MOLDING THE PARTS IN LEXAN 940.. some funny looking marks appearing after molding.. not sure how to solve it,.. i would be grate ful for any advise to help solve it
thanks & regards suresh.c
I have seen some strange flow marks that only got better with a hot mold....have you tried mold temps at 180 or hotter.... (not higher than your water lines will take though!)
Joel
MooCop
16th January 2018, 06:00 PM
I see that according to UL prospector, you should be aiming at a mold temp between 160 - 200F. I would attempt to hold at 190.