When you do a process window study, do you use melt temperature or mold temperature for the X-axis?
Mauricio
25th August 2011, 05:30 PM
Melt Temperature
ProcessEval
25th August 2011, 07:46 PM
I will use either depending on the processing range. If the melt temp range is small, I will use the mold temp.
skipmma
30th October 2012, 11:25 PM
I will use either depending on the processing range. If the melt temp range is small, I will use the mold temp.
If it is a Crystalline material then i use mold temp. If its an amorphous material i use melt temperature.