Process Window Study - Melt or Mold Temp?

[Suhas]

When you do a process window study, do you use melt temperature or mold temperature for the X-axis?

[Mauricio]

Melt Temperature

[ProcessEval]

I will use either depending on the processing range. If the melt temp range is small, I will use the mold temp.

[skipmma]

I will use either depending on the processing range. If the melt temp range is small, I will use the mold temp.

If it is a Crystalline material then i use mold temp. If its an amorphous material i use melt temperature.