Hi Rick!! Yes it is a thin wall IML high speed process. Recovery time takes around: 5.84s - 6.13s Im able to monitor recovery pressure it is...

And what was the problem?

So it appears this is a thin wall high speed press and process? I ask how long It takes screw to recover, do you have shut off nozzles in mold or on...

Here is a slide that I put together for our operators to explain each of these settings. Take a look and if you have any other questions let me know....

What is the width and depth of the tab gate? What is the part thickness at the gate? I think your gates should be much wider and the depth adjusted...

Hi Saeed, could you please post a new (next) photo of bloom area and Picture of injection diagram (injection pressure + screw speed/ position)? thanks

Thanks Rick, We have massive cross-sectional area through large underhung tab gates. No melt shear through these gates. We’ve tried all the gate...